IROGRAN® A 92 E 5670 FCM

Polyester-based Thermoplastic Polyurethane

Product Description:
IROGRAN® A 92 E 5670 FCM is a food contact approved polyester-based Thermoplastic Polyurethane (TPU) for melt calendering. Key features are abrasion resistance, excellent wear performance, good low temperature performance and high elasticity.
MAIN APPLICATIONS:
Thin wall extrusion profiles, textile lamination and calendering applications.

Details

At Jan.2016: US / EAIME / APAC MST / MTS / - finished 09.10.2016
Properties Key NORM Value Unit
Hardness (after 3 sec.) M ISO 7619 90 Shore A
Hardness (after 3 sec.) M ISO 7619 38 Shore D
Density M ISO 1183-1 1,21 g/cm³
Tensile strength M DIN 53504 40 MPa
Elongation @ break M DIN 53504 570 %
Tensile stress @ 100% elongation M DIN 53504 7,8 MPa
Tensile stress @ 300% elongation M DIN 53504 14,9 MPa
Tear strength M ISO 34-1 80 N/mm
Abrasion M ISO 4649 25 mm³
Bayshore rebound resilience M ASTM D 2632 30 %
Compression set at 70h @ 23°C M ISO 815 26 %
Compression set at 24h @ 70°C M ISO 815 46 %
Mold shrinkage M ISO 294-4 0,7 %
Softening range low E Huntsman TMA 145 °C
Softening range high E Huntsman TMA 160 °C
  • M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing

  • E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 10kg] ISO 1133-1  =  60 cm³/10min

Processing Parameter:   Extrusion
Temperature Profile °C
Feed Zone: 25 - 40
Barrel: 170 - 200
Die Head: 180 - 200
Nozzle: 175 - 205
Processing Parameter:   Calendering
Temperature Profile °C
Front Roll: 170 - 190
Rear Roll: 170 - 190