IROGRAN® A 85 C 5024

Polyester-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 85 C 5024 is a polyester-based Thermoplastic Polyurethane (TPU) for extrusion and injection molding applications. Key features are excellent wear performance, good low temperature performance and matte surface.

MAIN APPLICATIONS:

Thin wall technical parts, thin wall extrusion profiles and spiral hoses.

Details

At Jan.2016: US / EAIME / APAC - / MTO / MTS finished 08.10.2016

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ASTM D 2240	88	Shore A
Hardness (after 3 sec.)	M	ASTM D 2240	37	Shore D
Tensile strength	M	ASTM D 412	5200	psi
Elongation @ break	M	ASTM D 412	720	%
Tensile stress @ 100% elongation	M	ASTM D 412	940	psi
Tensile stress @ 300% elongation	M	ASTM D 412	1380	psi
Tear strength	M	ASTM D 624	560	pli
Abrasion	M	ISO 4649	44	mm³
Bayshore rebound resilience	M	ASTM D 2632	23	%
Compression set at 70h @ 23°C	M	ASTM D 395	22	%
Compression set at 22h @ 70°C	M	ASTM D 395	43	%
Mold shrinkage	M	ASTM D 955	1.0	%
Softening range low	E	Huntsman TMA	160	°C
Softening range high	E	Huntsman TMA	175	°C

M = Injection moulded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [195°C / 8,7kg] ISO 1133-1 = 40 cm³/10min

Processing Parameter:	Extrusion
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	170 - 200
Die Head:	170 - 200
Nozzle:	170 - 200

View Pdf-File