IROGRAN® A 98 H 4661

Polyester-based Thermoplastic Polyurethane

Product Description:
IROGRAN® A 98 H 4661 is a polyester-based Thermoplastic Polyurethane (TPU) for injection molding applications. Key features are excellent wear performance, resistance to dynamic stress and short cycle times.
MAIN APPLICATIONS:
Thick wall technical parts and thin wall technical parts.

Details

At Jan.2016: US / EAIME / APAC - / MTS / MTO finished 10.08.2016
Properties Key NORM Value Unit
Hardness (after 3 sec.) M ASTM D 2240 96 Shore A
Hardness (after 3 sec.) M ASTM D 2240 52 Shore D
Density M ASTM D 792 1.23 g/cm³
Tensile strength M ASTM D 412 5670 psi
Elongation @ break M ASTM D 412 610 %
Tensile stress @ 100% elongation M ASTM D 412 2390 psi
Tensile stress @ 300% elongation M ASTM D 412 2960 psi
Tear strength M ASTM D 624 970 pli
Abrasion M ISO 4649 35 mm³
Bayshore rebound resilience M ASTM D 2632 28 %
Compression set at 70h @ 23°C M ASTM D 395 25 %
Compression set at 24h @ 70°C M ASTM D 395 46 %
Mold shrinkage M ASTM D 955 0.7 %
Softening range low E Huntsman TMA 190 °C
Softening range high E Huntsman TMA 200 °C
  • M = Injection moulded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing

  • E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [210°C / 10kg] ISO 1133-1  =  60 cm³/10min

Processing Parameter:   Injection Molding
Temperature Profile °C
Feed Zone: 25 - 40
Barrel: 190 - 215
Nozzle: 200 - 215
Mold: 20 - 50
View Pdf-File