| Properties | Key | NORM | Value | Unit |
|---|---|---|---|---|
| Hardness (after 3 sec.) | M | ISO 7619 | 97 | Shore A |
| Hardness (after 3 sec.) | M | ISO 7619 | 50 | Shore D |
| Density | M | ISO 1183-1 | 1,16 | g/cm³ |
| Tensile strength | E | DIN 53504 | 3030 | MPa |
| Elongation @ break | E | DIN 53504 | 680 | % |
| Tensile stress @ 50% elongation | E | DIN 53504 | 1040 | MPa |
| Tensile stress @ 100% elongation | E | DIN 53504 | 1060 | MPa |
| Tensile stress @ 300% elongation | E | DIN 53504 | 1120 | MPa |
| Tear strength | E | ISO 34-1 | 510 | N/mm |
| Flexural modulus @ 23°C | M | ISO 178 | 39310 | MPa |
| Flexural modulus @ -29°C | M | ISO 178 | 180100 | MPa |
| Bayshore rebound resilience | M | ASTM D 2632 | 47 | % |
| Compression set at 22h @ 23°C | M | 64 | ||
| Softening range low | E | Huntsman TMA | 83 | °C |
| Softening range high | E | Huntsman TMA | 112 | °C |
| Glass transition temperature (DSC) | E | Huntsman | -41 | °C |
| Vicat softening point VST/A120 | M | ISO 306 | 47 | °C |
M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.