Polyether-based Thermoplastic Polyurethane
|Hardness (after 3 sec.)||M||ASTM D 2240||88||Shore A|
|Hardness (after 3 sec.)||M||ASTM D 2240||42||Shore D|
|Density||M||ASTM D 792||1.12||g/cm³|
|Tensile strength||E||ASTM D 412||8065||psi|
|Elongation @ break||E||ASTM D 412||530||%|
|Tensile stress @ 100% elongation||E||ASTM D 412||960||psi|
|Tensile stress @ 300% elongation||E||ASTM D 412||1900||psi|
|Tear strength||E||ASTM D 624||480||pli|
|Compression set at 22h @ 23°C||M||ASTM D 395||30||%|
|Compression set at 22h @ 70°C||M||ASTM D 395||80||%|
|Softening range low||E||Huntsman TMA||160||°C|
|Softening range high||E||Huntsman TMA||170||°C|
|Glass transition temperature (DSC)||E||ASTM D 3418||-37||°C|
M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.