Polyester-based Thermoplastic Polyurethane
Properties | Key | NORM | Value | Unit |
---|---|---|---|---|
Hardness (after 3 sec.) | M | ISO 7619 | 95 | Shore A |
Density | M | ISO 1183-1 | 1,18 | g/cm³ |
Softening range low | E | Huntsman TMA | 65 | °C |
Softening range high | E | Huntsman TMA | 70 | °C |
M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.
Melt Volume Rate [170°C / 10kg] ISO 1133-1 = 75 cm³/10min.
This IROSTIC grade can be used as a part of a reactive hotmelt system.
The processing temperature is 80°C.
Full bonding strength will be reached after 24 hours.