Aliphatic polyether-based Thermoplastic Polyurethane
|Hardness (after 3 sec.)||M||ASTM D 2240||60||Shore A|
|Hardness (after 3 sec.)||M||ASTM D 2240||15||Shore D|
|Density||M||ASTM D 792||1.04||g/cm³|
|Tensile strength||E||ASTM D 412||2170||psi|
|Elongation @ break||E||ASTM D 412||680||%|
|Tensile stress @ 50% elongation||E||ASTM D 412||240||psi|
|Tensile stress @ 100% elongation||E||ASTM D 412||310||psi|
|Tensile stress @ 300% elongation||E||ASTM D 412||540||psi|
|Tear strength||E||ASTM D 624||230||pli|
|Softening range low||E||Huntsman TMA||77||°C|
|Softening range high||E||Huntsman TMA||112||°C|
|Glass transition temperature (DMA)||E||ASTM D 5026||-51||°C|
|Vicat softening point VST/A120||M||ASTM D 1525||45||°C|
M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.