Aliphatic polyether-based Thermoplastic Polyurethane
|Hardness (after 3 sec.)||M||ASTM D 2240||75||Shore A|
|Hardness (after 3 sec.)||M||ASTM D 2240||34||Shore D|
|Density||M||ASTM D 792||1.07||g/cm³|
|Tensile strength||E||ASTM D 412||5500||psi|
|Elongation @ break||E||ASTM D 412||460||%|
|Tensile stress @ 50% elongation||E||ASTM D 412||340||psi|
|Tensile stress @ 100% elongation||E||ASTM D 412||480||psi|
|Tensile stress @ 300% elongation||E||ASTM D 412||1660||psi|
|Tear strength||E||ASTM D 624||240||pli|
|Softening range low||E||Huntsman TMA||86||°C|
|Softening range high||E||Huntsman TMA||123||°C|
|Glass transition temperature (DMA)||E||ASTM D 5026||-50||°C|
|Vicat softening point VST/A120||M||ASTM D 1525||51||°C|
M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.