IROGRAN® CA117-200

Polyester-based Thermoplastic Polyurethane

Product Description:
IROGRAN® CA117-200 is a polyester-based Thermoplastic Polyurethane (TPU) for extrusion applications. Key features are plasticizer-free, phthalate-free, excellent multilayer bonding, good low temperature performance and robust processing.
MAIN APPLICATIONS:
Textile lamination and adhesive films.
Properties Key NORM Value Unit
Hardness (after 3 sec.) M ASTM D 2240 93 Shore A
Hardness (after 3 sec.) M ASTM D 2240 50 Shore D
Density M ASTM D 792 1.15 g/cm³
Tensile strength E ASTM D 412 2900 psi
Elongation @ break E ASTM D 412 640 %
Tensile stress @ 50% elongation E ASTM D 412 960 psi
Tensile stress @ 100% elongation E ASTM D 412 980 psi
Tensile stress @ 300% elongation E ASTM D 412 1070 psi
Tear strength E ASTM D 624 520 pli
Flexural modulus @ 23°C M ASTM D 790 32110 psi
Flexural modulus @ -29°C M ASTM D 790 148650 psi
Bayshore rebound resilience M ASTM D 2632 44 %
Compression set at 22h @ 23°C M ASTM D 395 61 %
Softening range low E Huntsman TMA 71 °C
Softening range high E Huntsman TMA 93 °C
Glass transition temperature (DSC) E ASTM D 3418 -40 °C
Vicat softening point VST/A120 M ASTM D 1525 46 °C
  • M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.

  • E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 5 kg]  ISO 1133-1 =  45 cm³/10 min

Processing Parameter:   Extrusion
Temperature Profile °C
Feed Zone: 25 - 40
Barrel: 135 - 145
Adapter: 140 - 150
Die: 140 - 150