IROGRAN® A 92 P 4207

Polyether-based Thermoplastic Polyurethane

Product Description:
IROGRAN® A 92 P 4207 is a polyether-based Thermoplastic Polyurethane (TPU) for extrusion and injection molding applications. Key features are excellent hydrolysis and microbial resistance, good low temperature performance, short cycle times, high melt stability and a glossy surface.
MAIN APPLICATIONS:
Thick wall extrusion profiles, pneumatic tubes, spiral hoses, cable jacketing and film and sheet.

Details

At Jan.2016: US / EAIME / APAC - / MTS / MTS finished 09.10.2016
Properties Key NORM Value Unit
Hardness (after 3 sec.) M ASTM D 2240 92 Shore A
Hardness (after 3 sec.) M ASTM D 2240 46 Shore D
Density M ASTM D 792 1.13 g/cm³
Tensile strength E ASTM D 412 6300 psi
Elongation @ break E ASTM D 412 510 %
Tensile stress @ 100% elongation E ASTM D 412 1350 psi
Tensile stress @ 300% elongation E ASTM D 412 2670 psi
Tear strength E ASTM D 624 570 pli
Flexural modulus @ 23°C M ASTM D 790 7670 psi
Flexural modulus @ -29°C M ASTM D 790 38280 psi
Abrasion M ISO 4649 40 mm³
Taber abrasion H-18 wheel 1000g M ASTM D 3389 27 mg/1000 cycles
Bayshore rebound resilience M ASTM D 2632 40 %
Compression set at 22h @ 23°C M ASTM D 395 37 %
Compression set at 22h @ 70°C M ASTM D 395 77 %
Mold shrinkage M ASTM D 955 0.9 %
Softening range low E Huntsman TMA 175 °C
Softening range high E Huntsman TMA 192 °C
Glass transition temperature (DSC) E ASTM D 3418 -39 °C
Vicat softening point VST/A120 M ASTM D 1525 107 °C
  • M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.

  • E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 21,6kg] ISO 1133-1  =  20 cm³/10min

Processing Parameter:   Extrusion
Temperature Profile °C
Feed Zone: 25 - 40
Barrel: 185 - 200
Die Head: 195 - 205
Nozzle: 190 - 200