IROGRAN® A 85 P 4854

Polyether-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 85 P 4854 is a high flame-retardant, halogen-free, polyether-based Thermoplastic Polyurethane (TPU) for extrusion and injection molding applications. Key features are excellent hydrolysis and microbial resistance, excellent wear performance, robust processing and matte surface.

MAIN APPLICATIONS:

Thin wall technical parts, thin wall extrusion profiles, thick wall extrusion profiles and cable jacketing.

Details

At Jan.2016: US / EAIME / APAC - / MTS / MTS finished 09.10.2016

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ASTM D 2240	84	Shore A
Hardness (after 3 sec.)	M	ASTM D 2240	33	Shore D
Density	M	ASTM D 792	1.14	g/cm³
Tensile strength	E	ASTM D 412	3810	psi
Elongation @ break	E	ASTM D 412	590	%
Tensile stress @ 100% elongation	E	ASTM D 412	660	psi
Tensile stress @ 300% elongation	E	ASTM D 412	1170	psi
Tear strength	E	ASTM D 624	280	pli
Flexural modulus @ 23°C	M	ASTM D 790	4100	psi
Flexural modulus @ -29°C	M	ASTM D 790	14500	psi
Abrasion	M	ISO 4649	64	mm³
Bayshore rebound resilience	M	ASTM D 2632	48	%
Compression set at 22h @ 23°C	M	ASTM D 395	30	%
Compression set at 22h @ 70°C	M	ASTM D 395	69	%
Mold shrinkage	M	ASTM D 955	1.1	%
Softening range low	E	Huntsman TMA	151	°C
Softening range high	E	Huntsman TMA	172	°C
Glass transition temperature (DSC)	E	ASTM D 3418	-48	°C
Vicat softening point VST/A120	M	ASTM D 1525	70	°C
Certificates			UL 94 - V0

M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 21,6kg] ISO 1133-1 = 150 cm³/10min

Processing Parameter:	Extrusion
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	160 - 200
Die Head:	175 - 205
Nozzle:	170 - 200

View Pdf-File