IROGRAN® A 85 P 4666

Polyether-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 85 P 4666 is a flame-retardant, halogen-free, melamine-free, polyether-based Thermoplastic Polyurethane (TPU) for extrusion applications. Key features are excellent hydrolysis and microbial resistance, good oil and solvent resistance, excellent wear performance, resistance to dynamic stress, a glossy surface and the material can be crosslinked via electron beam processing to enhance its performance characteristics. .

MAIN APPLICATIONS:

Thin wall technical parts, thin wall extrusion profiles, spiral hoses and cable jacketing.

Details

At Jan.2016: US / EAIME / APAC - / MTS / MTO finished 09.10.2016 19.05.26 PB change UL and E-Beam

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ISO 48-4	84	Shore A
Hardness (after 3 sec.)	M	ISO 48-4	31	Shore D
Density	M	ISO 1183-1	1,15	g/cm³
Tensile strength	M	DIN 53504	35	MPa
Elongation @ break	M	DIN 53504	720	%
Tensile stress @ 100% elongation	M	DIN 53504	5,7	MPa
Tensile stress @ 300% elongation	M	DIN 53504	9,0	MPa
Tear strength	M	ISO 34-1	45	N/mm
Abrasion	M	ISO 4649	45	mm³
Bayshore rebound resilience	M	ASTM D 2632	45	%
Compression set at 70h @ 23°C	M	ISO 815	25	%
Compression set at 24h @ 70°C	M	ISO 815	42	%
Mold shrinkage	M	ISO 294-4	0,9	%
Softening range low	E	Huntsman TMA	155	°C
Softening range high	E	Huntsman TMA	170	°C
Certificates			UL 94 - V2

M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 21,6kg] ISO 1133-1 = 55 cm³/10min

Processing Parameter:	Extrusion
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	175 - 190
Die Head:	185 - 195
Nozzle:	170 - 180

The recommended electron beam dose is 150 kGr.