IROGRAN® A 80 P 5039

Polyether-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 80 P 5039 is a polyether-based Thermoplastic Polyurethane (TPU) for extrusion and injection molding applications. Key features are , excellent hydrolysis and microbial resistance, low hardness and modulus, good low temperature performance, robust processing and high transparency.

MAIN APPLICATIONS:

Thin wall technical parts, thick wall extrusion profiles, spiral hoses, cable jacketing and film and sheet.

Details

At Jan.2016: US / EAIME / APAC MTO / MTS / MTS finished 09.10.2016

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ASTM D 2240	81	Shore A
Hardness (after 3 sec.)	M	ASTM D 2240	33	Shore D
Density	M	ASTM D 792	1.10	g/cm³
Tensile strength	E	ASTM D 412	5660	psi
Elongation @ break	E	ASTM D 412	620	%
Tensile stress @ 100% elongation	E	ASTM D 412	680	psi
Tensile stress @ 300% elongation	E	ASTM D 412	1140	psi
Tear strength	E	ASTM D 624	380	pli
Flexural modulus @ 23°C	M	ASTM D 790	2450	psi
Flexural modulus @ -29°C	M	ASTM D 790	3390	psi
Abrasion	M	ISO 4649	34	mm³
Taber abrasion H-18 wheel 1000g	M	ASTM D 3389	6	mg/1000 cycles
Bayshore rebound resilience	M	ASTM D 2632	53	%
Compression set at 22h @ 23°C	M	ASTM D 395	27	%
Compression set at 22h @ 70°C	M	ASTM D 395	80	%
Mold shrinkage	M	ASTM D 955	1.3	%
Softening range low	E	Huntsman TMA	141	°C
Softening range high	E	Huntsman TMA	156	°C
Glass transition temperature (DSC)	E	ASTM D 3418	-40	°C
Vicat softening point VST/A120	M	ASTM D 1525	69	°C

M = Injection molded parts to meet DIN & ASTM requirements. Parts at room temperature aged prior to testing.
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 21.6 kg] ISO 1133-1 = 85 cm³/10 min

Processing Parameter:	Extrusion	Injection Molding
Temperature Profile	°C	°C
Feed:	25 - 40	25 - 40
Barrel:	165 - 190	175 - 195
Adapter/Nozzle:	175 - 200	180 - 200
Die/Mold:	175 - 200	20 - 50