IROGRAN® A 98 E 4066

Polyester-based Thermoplastic Polyurethane

Product Description:
IROGRAN® A 98 E 4066 is a polyester-based Thermoplastic Polyurethane (TPU) for injection molding applications. Key features are hydrolytically stabilized, abrasion resistance, excellent wear performance, resistance to dynamic stress, short cycle times, robust processing and high melt stability.
MAIN APPLICATIONS:
Thick wall technical parts and thin wall technical parts.

Details

At Jan.2016: US / EAIME / APAC - / MTS / - finished 09.10.2016
Properties Key NORM Value Unit
Hardness (after 3 sec.) M ISO 7619 97 Shore A
Hardness (after 3 sec.) M ISO 7619 49 Shore D
Density M ISO 1183-1 1,22 g/cm³
Tensile strength M DIN 53504 50 MPa
Elongation @ break M DIN 53504 530 %
Tensile stress @ 100% elongation M DIN 53504 14,0 MPa
Tensile stress @ 300% elongation M DIN 53504 25,0 MPa
Tear strength M ISO 34-1 135 N/mm
Abrasion M ISO 4649 30 mm³
Bayshore rebound resilience M ASTM D 2632 30 %
Compression set at 70h @ 23°C M ISO 815 30 %
Compression set at 24h @ 70°C M ISO 815 45 %
Mold shrinkage M ISO 294-4 0,7 %
Softening range low E Huntsman TMA 185 °C
Softening range high M Huntsman TMA 200 °C
  • M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing

  • E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [210°C / 21,6kg] ISO 1133-1  =  15 cm³/10min

Processing Parameter:   Injection Molding
Temperature Profile °C
Feed Zone: 25 - 40
Barrel: 190 - 210
Nozzle: 195 - 215
Mold: 20 - 50