Irogran A 80 P 5139 DP

Polyether-based Thermoplastic Polyurethane

Product Description:

Irogran A 80 P 5139 DP is a polyester-based Thermoplastic Polyurethane (TPU) for extrusion and injection molding applications. Key features are excellent hydrolysis and microbial resistance, low hardness and modulus, good low temperature performance, robust processing and high transparency.

MAIN APPLICATIONS:

Thin wall technical parts, thick wall extrusion profiles, spiral hoses, cable jacketing and film and sheet.

Details

New Version of the A80 P 5039

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ISO 7619	80	Shore A
Hardness (after 3 sec.)	M	ISO 7619	29	Shore D
Density	M	ISO 1183-1	1,10	g/cm³
Tensile strength	M	DIN 53504	32	MPa
Elongation @ break	M	DIN 53504	720	%
Tensile stress @ 100% elongation	M	DIN 53504	4,6	MPa
Tensile stress @ 300% elongation	M	DIN 53504	8,7	MPa
Tear strength	M	ISO 34-1	45	N/mm
Abrasion	M	ISO 4649	30	mm³
Bayshore rebound resilience	M	ASTM D 2632	47	%
Compression set at 70h @ 23°C	M	ISO 815	23	%
Compression set at 24h @ 70°C	M	ISO 815	43	%
Mold shrinkage	M	ISO 294-4	0,9	%
Softening range low	M	Huntsman TMA	145	°C
Softening range high	M	Huntsman TMA	155	°C

M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing

Processing Parameters

Melt Volume Rate [190°C / 21,6kg] ISO 1133-1 = 85 cm³/10min

Processing Parameter:	Extrusion
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	165 - 190
Die Head:	175 - 200
Nozzle:	170 - 200