| Properties | Key | NORM | Value | Unit |
|---|---|---|---|---|
| Hardness (after 3 sec.) | M | ISO 7619 | 94 | Shore A |
| Hardness (after 3 sec.) | M | ISO 7619 | 46 | Shore D |
| Density | M | ISO 1183-1 | 1,20 | g/cm³ |
| Tensile strength | M | DIN 53504 | 55 | MPa |
| Tensile stress @ 5% elongation | M | DIN 53504 | 8,2 | MPa |
| Tensile stress @ 20% elongation | M | DIN 53504 | 11 | MPa |
| Tensile stress @ 50% elongation | M | DIN 53504 | 12,5 | MPa |
| Tensile stress @ 300% elongation | M | DIN 53504 | 24,5 | MPa |
| Tear strength | M | ISO 34-1 | 110 | N/mm |
| Abrasion | M | ISO 4649 | 30 | mm³ |
| Bayshore rebound resilience | M | ASTM D 2632 | 29 | % |
| Compression set at 70h @ 23°C | M | ISO 815 | 15 | % |
| Compression set at 24h @ 70°C | M | ISO 815 | 25 | % |
| Compression set at 24h @ 100°C | M | ISO 815 | 30 | % |
| Compression set at 70h @ 100°C | M | ISO 815 | 35 | % |
| Mold shrinkage | M | ISO 294-4 | 1,3 | % |
| Softening range low | M | Huntsman TMA | 210 | °C |
| Softening range high | M | Huntsman TMA | 220 | °C |
| Vicat softening point VST/A120 | M | ISO 306 | 160 | °C |
M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 120 °C prior to testing
Melt Volume Rate [210°C / 21,6kg] ISO 1133-1 = 70 cm³/10min
| Processing Parameter: | Injection Molding |
| Temperature Profile | °C |
| Feed Zone: | 25 - 40 |
| Barrel: | 205 - 215 |
| Nozzle: | 210 - 220 |
| Mold: | 20 - 50 |