IROGRAN® A 70 H 4673M

Polyester-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 70 H 4673M is a polyester-based Thermoplastic Polyurethane (TPU) for injection molding applications. Key features are excellent wear performance, good low temperature performance, high elasticity, short cycle times and high transparency.

MAIN APPLICATIONS:

Thick wall technical parts and thin wall technical parts.

Details

At Jan.2016: US / EAIME / APAC - / MTS / MTO finished 08.10.2016

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ISO 7619	71	Shore A
Hardness (after 3 sec.)	M	ISO 7619	21	Shore D
Density	M	ISO 1183-1	1,15	g/cm³
Tensile strength	M	DIN 53504	35	MPa
Elongation @ break	M	DIN 53504	880	%
Tensile stress @ 100% elongation	M	DIN 53504	3,5	MPa
Tensile stress @ 300% elongation	M	DIN 53504	7,0	MPa
Tear strength	M	ISO 34-1	45	N/mm
Abrasion	M	ISO 4649	35	mm³
Bayshore rebound resilience	M	ASTM D 2632	50	%
Compression set at 70h @ 23°C	M	ISO 815	34	%
Compression set at 24h @ 70°C	M	ISO 815	48	%
Mold shrinkage	M	ISO 294-4	0,9	%
Softening range low	E	Huntsman TMA	145	°C
Softening range high	E	Huntsman TMA	170	°C

M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 5kg] ISO 1133-1 = 50 cm³/10min

Processing Parameter:	Injection Molding
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	170 - 180
Nozzle:	170 - 185
Mold:	20 - 50