Polyester-based Thermoplastic Polyurethane
|Solution viscosity range - 1.6||V1||Huntsman||140 - 180||mPa*s|
|Solution viscosity range - 05||V1||Huntsman||400 - 600||mPa*s|
|Solution viscosity range - 12||V1||Huntsman||1000 - 1400||mPa*s|
|Minimum activation temperature||Huntsman||60 - 65||°C|
|Type of use||2 component|
V1 = viscosity (Brookfield RVT) at 20°C for 15% solid in MEK.
This IROSTIC grade can be used as a 2-component system in combination with our IRODUR product range.
Clean and dry parts to be bonded.
If possible, roughen the two surfaces using abrasive material.
Apply a thin layer of adhesive solution.
Dry surfaces for approx. 30 min to allow solvent evaporation.
Activate both surfaces by warming up to 60 - 65°C.
Press surfaces together for 30 seconds.
The bonding is stable after approx. 1 minute.
Full bonding strength will be reached after 24 hours.
Please note that the procedure described here is for the adhesive solution prepared with the IROSTIC.