IROGRAN® A 85 P 4394 UV

Polyether-based Thermoplastic Polyurethane

Product Description:

IROGRAN® A 85 P 4394 UV is a polyether-based Thermoplastic Polyurethane (TPU) for extrusion and injection molding applications. Key features are excellent hydrolysis and microbial resistance, improved UV stability, excellent wear performance and a glossy surface.

MAIN APPLICATIONS:

Thick wall technical parts, thick wall extrusion profiles, spiral hoses, cable jacketing and film and sheet.

Details

At Jan.2016: US / EAIME / APAC MTS / - / - finished 09.10.2016

Properties	Key	NORM	Value	Unit
Hardness (after 3 sec.)	M	ISO 7619	85	Shore A
Hardness (after 3 sec.)	M	ISO 7619	40	Shore D
Density	M	ISO 1183-1	1.12	g/cm³
Tensile strength	M	DIN 53504	45	MPa
Elongation @ break	M	DIN 53504	650	%
Tensile stress @ 100% elongation	M	DIN 53504	7	MPa
Tensile stress @ 300% elongation	M	DIN 53504	12	MPa
Tear strength	M	ISO 34-1	60	N/mm
Abrasion	M	ISO 4649	25	mm³
Bayshore rebound resilience	M	ASTM D 2632	36	%
Compression set at 70h @ 23°C	M	ISO 815	20	%
Compression set at 24h @ 70°C	M	ISO 815	40	%
Mold shrinkage	M	ISO 294-4	0.8	%
Softening range low	E	Huntsman TMA	150	°C
Softening range high	E	Huntsman TMA	170	°C

M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing
E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 21,6kg] ISO 1133-1 = 65 cm³/10min

Processing Parameter:	Extrusion
Temperature Profile	°C
Feed Zone:	25 - 40
Barrel:	165 - 200
Die Head:	175 - 205
Nozzle:	170 - 200

View Pdf-File