IROGRAN® A 65 P 4324N

Polyether-based Thermoplastic Polyurethane

Product Description:
IROGRAN® A 65 P 4324N is a polyether-based Thermoplastic Polyurethane (TPU) for injection molding applications. Key features are phthalate-free, excellent surface definition, excellent wear performance, good low temperature performance and high elasticity.
MAIN APPLICATIONS:
Thick wall technical parts and thin wall technical parts.

Details

At Jan.2016: US / EAIME / APAC - / MTS / MTO finished 09.10.2016
Properties Key NORM Value Unit
Hardness (after 3 sec.) M ISO 7619 71 Shore A
Hardness (after 3 sec.) M ISO 7619 22 Shore D
Density M ISO 1183-1 1,12 g/cm³
Tensile strength M DIN 53504 30 MPa
Elongation @ break M DIN 53504 800 %
Tensile stress @ 100% elongation M DIN 53504 3,9 MPa
Tensile stress @ 300% elongation M DIN 53504 9,8 MPa
Tear strength M ISO 34-1 35 N/mm
Abrasion M ISO 4649 60 mm³
Bayshore rebound resilience M ASTM D 2632 58 %
Compression set at 70h @ 23°C M ISO 815 25 %
Compression set at 24h @ 70°C M ISO 815 48 %
Mold shrinkage M ISO 294-4 1,2 %
Softening range low E Huntsman TMA 110 °C
Softening range high E Huntsman TMA 165 °C
  • M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing

  • E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 10kg] ISO 1133-1  =  60 cm³/10min

Processing Parameter:   Injection Molding
Temperature Profile °C
Feed Zone: 25 - 40
Barrel: 170 - 180
Nozzle: 175 - 185
Mold: 20 - 50
View Pdf-File