IROGRAN® A 92 C 4959

Polyester-based Thermoplastic Polyurethane

Product Description:
IROGRAN® A 92 C 4959 is a polyester-based Thermoplastic Polyurethane (TPU) for extrusion applications. Key features are excellent wear performance, good low temperature performance and high elasticity.
MAIN APPLICATIONS:
Thin wall extrusion profiles and spiral hoses.

Details

At Jan.2016: US / EAIME / APAC - / MTO / MTS finished 08.10.2016
Properties Key NORM Value Unit
Hardness (after 3 sec.) M ISO 7619 91 Shore A
Hardness (after 3 sec.) M ISO 7619 40 Shore D
Density M ISO 1183-1 1,23 g/cm³
Tensile strength M DIN 53504 43 MPa
Elongation @ break M DIN 53504 600 %
Tensile stress @ 100% elongation M DIN 53504 7,9 MPa
Tensile stress @ 300% elongation M DIN 53504 13,50 MPa
Tear strength M ISO 34-1 90 N/mm
Abrasion M ISO 4649 25 mm³
Bayshore rebound resilience M ASTM D 2632 29 %
Compression set at 70h @ 23°C M ISO 815 20 %
Compression set at 24h @ 70°C M ISO 815 40 %
Mold shrinkage M ISO 294-4 0,7 %
Softening range low E Huntsman TMA 165 °C
Softening range high E Huntsman TMA 180 °C
  • M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing

  • E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [205°C / 8,7kg] ISO 1133-1  =  60 cm³/10min

Processing Parameter:   Extrusion
Temperature Profile °C
Feed Zone: 25 - 40
Barrel: 195 - 210
Die Head: 195 - 210
Nozzle: 195 - 210
View Pdf-File