IROGRAN® A 87 H 4615

Polyester-based Thermoplastic Polyurethane

Product Description:
IROGRAN® A 87 H 4615 is a polyester-based Thermoplastic Polyurethane (TPU) for injection molding applications. Key features are plasticizer-free, excellent wear performance, resistance to dynamic stress, high elasticity and robust processing.
MAIN APPLICATIONS:
Thick wall technical parts and thin wall technical parts.

Details

At Jan.2016: US / EAIME / APAC MTS / MTS / MTO finished 08.10.2016 08/17/2021 by Lidina Canuto: Updated existing data which is based on the DIN/ISO since this is German made, but remove ASTM data. Reason: Ringwood’s A 87 H 4615 formulation is distinctly different from OSN made. RWD uses a mix polyol approach while OSN made material uses only 1 polyol.
Properties Key NORM Value Unit
Hardness (after 3 sec.) M ISO 7619 85 Shore A
Hardness (after 3 sec.) M ISO 7619 35 Shore D
Density M ISO 1183-1 1,20 g/cm³
Tensile strength M DIN 53504 45 MPa
Elongation @ break M DIN 53504 640 %
Tensile stress @ 100% elongation M DIN 53504 5,6 MPa
Tensile stress @ 300% elongation M DIN 53504 11,1 MPa
Tear strength M ISO 34-1 80 N/mm
Abrasion M ISO 4649 25 mm³
Bayshore rebound resilience M ASTM D 2632 40 %
Compression set at 70h @ 23°C M ISO 815 25 %
Compression set at 24h @ 70°C M ISO 815 43 %
Mold shrinkage M ISO 294-4 1,1 %
Softening range low E Huntsman TMA 135 °C
Softening range high E Huntsman TMA 185 °C
  • M = Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs @ 100 °C prior to testing

  • E = Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.

Processing Parameters

Melt Volume Rate [190°C / 21,6kg] ISO 1133-1  =  50 cm³/10min

Processing Parameter:   Injection Molding
Temperature Profile °C
Feed Zone: 25 - 40
Barrel: 175 - 190
Nozzle: 180 - 200
Mold: 20 - 50